Biomechanical, histological and histomorphometric analyses of calcium phosphate cement compared to PMMA for vertebral augmentation in a validated animal model
verfasst von:
Luis Alvarez Galovich, Antonio Perez-Higueras, Jose R. Altonaga, José Manuel Gonzalo Orden, Maria Lluisa Mariñoso Barba, Maria Teresa Carrascal Morillo
Erschienen in:
European Spine Journal
|
Sonderheft 3/2011
Einloggen, um Zugang zu erhalten
Abstract
Introduction
Calcium phosphate cements (biocements) are alternative materials for use in vertebral augmentation procedures, and are a potential solution to problems associated with polymethylmethacrylate (PMMA) cements. The aim of this study is to demonstrate the utility of percutaneously injected biocements compared with PMMA in a validated animal model of osteoporosis.
Materials and methods
Fortyseven augmentation procedures were performed on 11 osteoporotic sheep. 9 vertebrae were augmented with PMMA and 38 with a biocement. The animals were killed in four groups: at 7 days, 3 months, 6 months, and 1 year after intervention. Radiological study and TC of the pieces were obtained to evaluate for leakage, cement diffusion, and integration. In total, 26 biomechanic studies and 27 histomorphometry analyses were performed, included control vertebrae.
Results
In 20.9% of the vertebrae, the hole was empty at sacrifice. The pattern of fracture was heterogeneous, and cement augmentation did not increase vertebral strength or decrease vertebral stiffness compared to control vertebrae, with neither PMMA or biocement. The rate of remodeling of the biocement was not predictable. In the single majority, there is peripheral remodeling, staying the volume of injected biocement stable.
Conclusions
Even though this animal model may not be useful to analyze the biomechanical pattern of treated vertebrae, it demonstrates that the percutaneous use of biocements in vertebral augmentation techniques is not predictable. This is one reason not to recommend its use presently as a substitute for PMMA in vertebral reinforcement procedures.