In Vitro Assessment of Fluorine Nanoemulsion-Labeled Hyaluronan-Based Hydrogels for Precise Intrathecal Transplantation of Glial-Restricted Precursors
verfasst von:
Marcin Piejko, Piotr Walczak, Xiaowei Li, Jeff W. M. Bulte, Miroslaw Janowski
Erschienen in:
Molecular Imaging and Biology
|
Ausgabe 6/2019
Einloggen, um Zugang zu erhalten
Abstract
Purpose
We studied the feasibility of labeling hydrogel scaffolds with a fluorine nanoemulsion for 19F- magnetic resonance imaging (MRI) to enable non-invasive visualization of their precise placement and potential degradation.
Procedure
Hyaluronan-based hydrogels (activated hyaluronan, HA) with increasing concentrations of fluorine nanoemulsion (V-sense) were prepared to measure the gelation time and oscillatory stress at 1 h and 7 days after the beginning of gelation. All biomechanical measurements were conducted with an ARES 2 rheometer. Diffusion of fluorine from the hydrogel: Three hydrogels in various Vs to HA volumetric ratios (1:50, 1:10, and 1:5) were prepared in duplicate. Hydrogels were incubated at 37 °C. To induce diffusion, three hydrogels were agitated at 1000 rpm. 1H and 19F MRI scans were acquired at 1, 3, 7 days and 2 months after gel preparation on a Bruker Ascend 750 scanner. To quantify fluorine content, scans were analyzed using Voxel Tracker 2.0. Assessment of cell viability in vitro and in vivo: Luciferase-positive mouse glial-restricted progenitors (GRPs) were embedded in 0:1, 1:50, 1:10, and 1:5 Vs:HA mixtures (final cell concentration =1 × 107/ml). For the in vitro assay, mixtures were placed in 96-wells plate in triplicate and bioluminescence was measured after 1, 3, 7, 14, 21, and 28 days. For in vivo experiments, Vs/HA mixtures containing GRPs were injected subcutaneously in SCID mice and BLI was acquired at 1, 3, 7, and 14 days post-injection.
Results
Mixing of V-sense at increasing ratios of 1:50, 1:10, and 1:5 v/v of fluorine/activated hyaluronan (HA) hydrogel gradually elongated the gelation time from 194 s for non-fluorinated controls to 304 s for 1:5 V-sense:HA hydrogels, while their elastic properties slightly decreased. There was no release of V-sense from hydrogels maintained in stationary conditions over 2 months. The addition of V-sense positively affected in vitro survival of scaffolded GRPs in a dose-dependent manner.
Conclusions
These results show that hydrogel fluorination does not impair its beneficial properties for scaffolded cells, which may be used to visualize scaffolded GRP transplants with 19F MRI.