Application of layered poly (L-lactic acid) cell free scaffold in a rabbit rotator cuff defect model

verfasst von: Atsuyuki Inui, Takeshi Kokubu, Hiroyuki Fujioka, Issei Nagura, Ryosuke Sakata, Hanako Nishimoto, Masaru Kotera, Takashi Nishino, Masahiro Kurosaka

Erschienen in: BMC Sports Science, Medicine and Rehabilitation | Ausgabe 1/2011

Abstract

Background

This study evaluated the application of a layered cell free poly (L-lactic acid) (PLLA) scaffold to regenerate an infraspinatus tendon defect in a rabbit model. We hypothesized that PLLA scaffold without cultivated cells would lead to regeneration of tissue with mechanical properties similar to reattached infraspinatus without tendon defects.

Methods

Layered PLLA fabric with a smooth surface on one side and a pile-finished surface on the other side was used. Novel form of layered PLLA scaffold was created by superimposing 2 PLLA fabrics. Defects of the infraspinatus tendon were created in 32 rabbits and the PLLA scaffolds were transplanted, four rabbits were used as normal control. Contralateral infraspinatus tendons were reattached to humeral head without scaffold implantation. Histological and mechanical evaluations were performed at 4, 8, and 16 weeks after operation.

Results

At 4 weeks postoperatively, cell migration was observed in the interstice of the PLLA fibers. Regenerated tissue was directly connected to the bone composed mainly of type III collagen, at 16 weeks postoperatively. The ultimate failure load increased in a time-dependent manner and no statistical difference was seen between normal infraspinatus tendon and scaffold group at 8 and 16 weeks postoperatively. There were no differences between scaffold group and reattach group at each time of point. The stiffness did not improve significantly in both groups.

Conclusions

A novel form of layered PLLA scaffold has the potential to induce cell migration into the scaffold and to bridge the tendon defect with mechanical properties similar to reattached infraspinatus tendon model.
Hinweise

Electronic supplementary material

The online version of this article (doi:10.​1186/​1758-2555-3-29) contains supplementary material, which is available to authorized users.

Competing interests

The authors declare that they have no competing interests.

Authors' contributions

TK, HF and MK conceived the study, and participated in its design and coordination. AI performed the statistical analysis and drafted the manuscript. IN, RS, and HN performed the animal experiment and mechanical evaluation. MK and TN provided the PLLA fabric. All authors read and approved the final manuscript.

Background

Rotator cuff tear is a common problem that may cause chronic pain with functional disability. If intolerable pain or functional disability persists, surgical treatment can be considered. Excellent outcomes have been reported with arthroscopic rotator cuff repair in small or medium sized tears [1], but large or massive rotator cuff tears are challenging for surgeons [2]. Surgical procedures are available for repair of massive rotator cuff tears including musculotendinous transfer [3] and patch grafting using fascial tissue [4] or synthetic materials [58], but these techniques have disadvantages. Tendon transfer is not an anatomical reconstruction and patch grafting using fascial tissue requires sacrifice of normal tissue. Using extracellular matrix derived from animals such as porcine small intestinal submucosa can cause an immune reaction and carry the risk of zoonoses resulting from xenotransplantation [9]. Nonabsorbable synthetic materials have been used [10], but foreign body reaction and bone erosion has been reported several years after surgery [11].
In tendon regeneration filed, tissue engineering using scaffolds, cultured cells and growth factors has been showing great advantage [12]. In a controlled laboratory study on rabbit model, fibroblast-seeded scaffolds showed better results compared to the scaffold alone in rotator cuff regeneration [6]. However, these methods require 2-stage surgeries; a first surgery to harvest cells and a second to transplant them. Since 2-step surgeries are considered invasive, less invasive methods need to be developed. If the scaffold could induce cells from the surrounding tissues, pre-expansion of the cells for the transplantation would not be required. The authors assessed a double layered form of bioabsorbable poly (L-lactic acid) (PLLA) fabric which have smooth surface on one side and pile-finished surface on the other side, and reported its potency for regenerations of tendons and ligaments in a rabbit model [13]. The author hypothesized that PLLA scaffold without cultivated cells would lead to regeneration of tissue with mechanical properties similar to reattached infraspinatus without tendon defects. In the current study, application of the layered PLLA scaffold was evaluated for the regeneration of rotator cuff tears in a rabbit model.

Methods

All the animal experiments were approved by the Animal Research Committee.

Preparation of Layered PLLA Scaffold

PLLA fibers (molecular weight, 86000; diameter, 23 μm) were textured into double layered fabric which had a smooth surface on one side and a rough (pile-finished) surface on the other side (Figure 1a). The fabric was cut to 5 × 10 mm pieces, two pieces were superimposed with the smooth surface outside and the rough surface inside. The both edges of the superimposed pieces were bonded by thermocompression. This tubular shaped fabric had layered structure, smooth outside and pile finished inside. Each tubular fabric was sterilized and used as layered scaffolds (Figure 1b).

Scaffold Implantation

Thirty two female Japanese white rabbits (2.7-3.5 kg) were administered intravenous pentobarbital (30 mg/kg). The surgical area was disinfected and 3 ml of 1% lidocaine was injected subcutaneously. A 3 cm incision was made on the right shoulder and the infraspinatus tendon was exposed. Rotator cuff defects were created by resecting the infraspinatus tendon (5 mm in width and 5 mm in length) from the greater tuberosity, and the scaffolds were transplanted to repair this defect. The proximal edge of the scaffold was sutured to the midsubstance of the tendon by 4-0 nylon suture. Decortication was performed at the greater tuberosity of the humeral head (1 mm depth and 5 mm length) and the distal edge of the scaffold was fixed to the bone by 4-0 nylon suture (Figure 2). After repairing the defect, the muscle and skin was sutured in separate layers. In the contralateral shoulder infraspinatus tendon was resected without creating a defect and the edge of tendon was sutured directly to the humeral head by 4-0 nylon suture as a control. Rabbits were allowed free cage movement after the operation. Rabbits were euthanized with an intravenous fatal dose of sodium pentobarbital and infraspinatus tendon humeral head complex was excised. For macroscopic and histological evaluations, 4 rabbits were randomly selected at 4, 8, and 16 weeks after the operation. For mechanical analysis, 4 rabbits were randomly selected at 0, 4, 8, and 16 weeks after the operation. Four rabbits did not undergo surgery were examined mechanically as normal controls.

Histological Analysis

After the macroscopic examination, the infraspinatus tendon humeral head complex was fixed in 4% paraformaldehyde, decalcified with 0.25 mol/l ethylenediaminetetraacetic acid in a phosphate buffered saline (pH 7.5), and embedded in paraffin. Sagittal sections (7 μm) were cut through the entire thickness of the defect, and stained with hematoxylin eosin (HE) then examined by light microscopy. For immunohistochemical analysis of type I and III collagens, deparaffinized sections were digested with proteinase (Dako Cytomation, Inc., CA, USA) for 10 minutes and treated with 3% hydrogen peroxide (WAKO Pure Chemical Industries, Ltd., Osaka, Japan) to block endogenous peroxidase activity. The sections were incubated with a 1:50 dilution of goat anti-type I or III collagen antibodies (Southern Biotechnology Associates Inc., AL, USA) at 4°C overnight and subsequently treated with peroxidase labeled anti-goat immunoglobulin (Histofine Simplestain max PO(G), Nichirei Bioscience, Tokyo, Japan) at room temperature for 30 minutes. The signal was developed using peroxidase substrate 3, 3-diaminobenzide (Histofine Simplestain DAB Solution, Nichirei Bioscience, Tokyo, Japan) and the sections were examined microscopically.

Mechanical Analysis

The infraspinatus tendon humeral head complex was harvested from each shoulder and all soft tissue except for the infraspinatus tendon was resected by sharp dissection. The humerus was potted in specially designed devices using polymethylmethacrylate (PMMA) resin and a specially designed device clamped the end of each tendon. The complex was placed vertically to a tensile sensor (AG-I SHIMAZU Co, Kyoto, Japan). Before the tensile test was conducted, the infraspinatus tendon humeral head complex was preconditioned with a static preload of 0.5 N for 5 minutes, followed by 10 cycles of loading and unloading at strain amplitude of approximately 0.5% at a rate of 20 mm per minute. Immediately after preconditioning, the ultimate load to failure was recorded in uniaxial tension at 20 mm per minute [14]. The ultimate load to failure and the stiffness were measured from load-deformation curve. Mechanical properties of normal infraspinatus tendon and scaffold itself were evaluated in the same manner.

Statistical Analysis

The paired t test was used to compare the mechanical properties of PLLA scaffold repair with the reattached tendon. Dunnett's test was used to compare the mechanical properties at each time point. A significance level of p < .05 was used. All data are presented as mean (SD).

Results

Histological Findings

No gross evidence of infection was noted at the surgical site throughout the experiment, and all defects with the implanted layered PLLA scaffolds were covered with smooth fibrous tissue. At 4 weeks, after the operation, the scaffold persisted and spindle shaped cells were observed inside the pile-finished PLLA fibers (Figure 3a). At the interface of the scaffold and bone, which could be detected clearly, some fibrous tissue was observed inside of the scaffold (Figure 3d). At 8 weeks after the operation, spindle cells were observed inside the scaffold (Figure 3b), and regenerated tissue was directly connected to the bone with irregular alignment of the cells at the scaffold-bone interface (Figure 3e). At 16 weeks after operation, fibrous tissue like collagenous fibers were observed inside the scaffold and some of the fiber started to be absorbed (Figure 3c). Fibrous tissue connected to the bone at the tendon-bone interface, however chondrogenesis were not seen and a enthesis was not regenerated (Figure 3f). Some multinuclear cells were seen inside the scaffold at each time point. Type I collagen was not detected inside of the scaffold (Figure 4a), but type III collagen was mainly detected in regenerated tissue in the scaffold and fibrous tissue that covered the scaffold (Figure 4b).

Mechanical Properties of Regenerated Tissue

Mechanical examination revealed that the ultimate failure load of the scaffold group was 21.3 (4.2) N, 52 (14.7) N, 69 (8.4) N, and 68.8 (12.7) N at 0, 4, 8, and 16 weeks after the operation, respectively. The reattach group values were 16.9 (6) N, 61.7 (9.5) N, 78 (26.3) N, and 69.4 (14.9) N at 0, 4, 8, and 16 weeks after the operation, respectively. All samples were broken at the scaffold bone interface. The ultimate failure load of normal infraspinatus tendon was 70.6 (8.6) N and that of scaffold itself was 30.7 (6.2) N. The value obtained in the week immediately after the operation (week 0) mainly represents the mechanical property of the scaffold/suture construct. The ultimate failure load was weaker in the scaffold group at 4 weeks after the operation than normal infraspinatus tendon, but the ultimate failure load of scaffold group increased in a time-dependent manner and the difference between the scaffold group and normal infraspinatus tendon at 8 and 16 weeks was not statistically significant. In addition, there was no significant difference between the scaffold group and the reattach group at each time point (Figure 5a). On the other hand, the stiffness of the scaffold group was 2.6 (0.46) N/mm, 7.8 (2.5) N/mm, 8.1 (2.5) N/mm, and 11.1 (3.1) N/mm at 0, 4, 8, and 16 weeks after the operation, respectively. The reattach group values were 2.42 (0.32) N/mm, 7.3 (2.6) N/mm, 11.0 (3.1) N/mm, and 10.2 (1.4) N/mm at 0, 4, 8, and 16 weeks after the operation, respectively. The stiffness of normal infraspinatus tendon was 16.1 (3.4) N/mm and that of scaffold itself was 11.6 (4.2) N/mm. The stiffness of the scaffold group increased in a time-dependent manner, but it remained less stiff than the normal infraspinatus tendon at each time point. The stiffness was not significantly different between the scaffold group and the reattach group at each time point (Figure 5b).

Discussion

Several synthetic materials have been previously used in rotator cuff regeneration. Implantation of polytetrafuluoroethylene (PTFE) patch grafts showed satisfactory functional results in 23 out of 25 patients with massive rotator cuff tears [10]. However, reconstruction of rotator cuff defects with PTFE in a canine model showed foreign body reaction at 12-24 weeks after surgery and bone resorption at the insertion of the PTFE into the bone [11]. Chitin fabric used as a scaffold in rabbit rotator cuff tears resulted in regenerated tissue, mainly composed by type III collagen [7]. Finally, poly glycolic acid (PGA) sheets used as a scaffold showed a well-arranged fibrocartilage layer in regenerated tendon insertions [8].
All the scaffolds previously used for rotator cuff tears had a uniform structure [58, 10, 11]. The authors previously reported the potency of double layered PLLA fabric which has smooth surface on one side and pile-finished surface on the other side for tendon tissue engineering. In its pile-finished side, cell migration was observed. On the other hand, smooth side showed less adhesion. The double layered fabric maintained its mechanical property compared with plain-woven fabric [13]. In present study, the authors chose this PLLA fabric as the scaffold material for rotator cuff repair study. A substantial amount of spindle shaped cells migrated inside the layered scaffold. The authors also noted several giant polynuclear cells indicative of an inflammatory reaction.
PLLA fiber is an organic polymer from L-lactate that dissolves in H2O and CO2. PLLA was used as a material for human orthopedic implants [15] and as synthetic material in ligament or tendon tissue engineering research [16]. An in vitro study that compared PGA, poly-L-lactate-epsilon-caprolactone (PLC), and PLLA scaffolds concluded that PLLA and PLC scaffolds provided the best material for tendon regeneration because of slow absorption rates and better mechanical properties [17]. Augmentation of rotator cuff repair with a PLLA scaffold provided sufficient initial strength in a sheep model [16], but the byproducts of PLLA degradation might have inhibited the tendon from healing to bone [18]. In present study, the ultimate failure load of the scaffold group increased over time and was not different from normal infraspinatus tendon 8 weeks after surgery. No difference was observed between the scaffold group and reattachment control group, indicating that the implantation of the layered PLLA scaffold in rotator cuff defect had same strength as reattachment. Thus the authors could confirm our hypothesis that PLLA scaffold without cultivated cells would lead to regeneration of tissue with mechanical properties similar to reattached infraspinatus without tendon defects. However, the stiffness was weaker in the scaffold group than normal infraspinatus tendon, indicating that the regenerated tissue had not matured as a normal tendon. While type I collagen is prominent in the normal rotator cuff tendon, type III collagen is expressed during the tendon healing process and its levels decrease as the tendon matures [19, 20]. Therefore, if the regenerated tissues mainly consist of type III collagen, the mechanical property of these tissues is presumably inferior to the native tissues [2123]. Dominant expression of type III collagen was observed, which may have been caused by the low absorption rate of the PLLA fiber that can lead to inferior stiffness properties compared with normal infraspinatus tendon.
There were some limitations in this study. Firstly, the anatomy of a rabbit's shoulder differs from the human rotator cuff because the short rotator muscles of rabbits do not form a rotator cuff as in humans. Secondly, the rabbit model in present study differs from chronic rotator cuff injury model. Thirdly, the PLLA scaffold can induce an inflammatory reaction. Clinical studies showed that a systemic or local reaction might arise. Although the degradation products of PLLA are natural metabolites, they are acidic [14, 24]. The absorption rate of the scaffold must be taken into consideration and long-term follow up is required to confirm results.

Conclusions

A novel form of layered PLLA scaffold was used to repair rotator cuff defect in a rabbit model. This layered form of the PLLA scaffold has the potential to induce cell migration and to fill the gap between the bone and the tendon stump, with mechanical properties similar to reattached infraspinatus.

Acknowledgements

This study was supported in part by the ministry of Education, Culture, Sports, Science and Technology-Japan grants No.197912030 for aiding scientific researchers.
This article is published under license to BioMed Central Ltd. This is an Open Access article distributed under the terms of the Creative Commons Attribution License (http://​creativecommons.​org/​licenses/​by/​2.​0), which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

Competing interests

The authors declare that they have no competing interests.

Authors' contributions

TK, HF and MK conceived the study, and participated in its design and coordination. AI performed the statistical analysis and drafted the manuscript. IN, RS, and HN performed the animal experiment and mechanical evaluation. MK and TN provided the PLLA fabric. All authors read and approved the final manuscript.
Literatur
1.
Zurück zum Zitat Morse K, Davis AD, Afra R, Kaye EK, Schepsis A, Voloshin I: Arthroscopic versus mini-open rotator cuff repair: a comprehensive review and meta-analysis. Am J Sports Med. 2008, 36: 1824-1828. 10.1177/0363546508322903.CrossRefPubMed Morse K, Davis AD, Afra R, Kaye EK, Schepsis A, Voloshin I: Arthroscopic versus mini-open rotator cuff repair: a comprehensive review and meta-analysis. Am J Sports Med. 2008, 36: 1824-1828. 10.1177/0363546508322903.CrossRefPubMed
2.
Zurück zum Zitat Zumstein MA, Jost B, Hempel J, Hodler J, Gerber C: The clinical and structural long-term results of open repair of massive tears of the rotator cuff. J Bone Joint Surg Am. 2008, 90: 2423-2431. 10.2106/JBJS.G.00677.CrossRefPubMed Zumstein MA, Jost B, Hempel J, Hodler J, Gerber C: The clinical and structural long-term results of open repair of massive tears of the rotator cuff. J Bone Joint Surg Am. 2008, 90: 2423-2431. 10.2106/JBJS.G.00677.CrossRefPubMed
3.
Zurück zum Zitat Karas SE, Giachello TL: Subscapularis transfer for reconstruction of massive tears of the rotator cuff. J Bone Joint Surg Am. 1996, 78: 239-245.PubMed Karas SE, Giachello TL: Subscapularis transfer for reconstruction of massive tears of the rotator cuff. J Bone Joint Surg Am. 1996, 78: 239-245.PubMed
4.
Zurück zum Zitat Sano H, Kumagai J, Sawai T: Experimental fascial autografting for the supraspinatus tendon defect: remodeling process of the grafted fascia and the insertion into bone. J Shoulder Elbow Surg. 2002, 11: 166-173. 10.1067/mse.2002.120808.CrossRefPubMed Sano H, Kumagai J, Sawai T: Experimental fascial autografting for the supraspinatus tendon defect: remodeling process of the grafted fascia and the insertion into bone. J Shoulder Elbow Surg. 2002, 11: 166-173. 10.1067/mse.2002.120808.CrossRefPubMed
5.
Zurück zum Zitat Aoki M, Miyamoto S, Okamura K, Yamashita T, Ikada Y, Matsuda S: Tensile properties and biological response of poly(L-lactic acid) felt graft: an experimental trial for rotator-cuff reconstruction. J Biomed Mater Res B Appl Biomater. 2004, 71: 252-259.CrossRefPubMed Aoki M, Miyamoto S, Okamura K, Yamashita T, Ikada Y, Matsuda S: Tensile properties and biological response of poly(L-lactic acid) felt graft: an experimental trial for rotator-cuff reconstruction. J Biomed Mater Res B Appl Biomater. 2004, 71: 252-259.CrossRefPubMed
6.
Zurück zum Zitat Funakoshi T, Majima T, Iwasaki N, Suenaga N, Sawaguchi N, Shimode K, Minami A, Harada K, Nishimura S: Application of tissue engineering techniques for rotator cuff regeneration using a chitosan-based hyaluronan hybrid fiber scaffold. Am J Sports Med. 2005, 33: 1193-1201. 10.1177/0363546504272689.CrossRefPubMed Funakoshi T, Majima T, Iwasaki N, Suenaga N, Sawaguchi N, Shimode K, Minami A, Harada K, Nishimura S: Application of tissue engineering techniques for rotator cuff regeneration using a chitosan-based hyaluronan hybrid fiber scaffold. Am J Sports Med. 2005, 33: 1193-1201. 10.1177/0363546504272689.CrossRefPubMed
7.
Zurück zum Zitat Funakoshi T, Majima T, Suenaga N, Iwasaki N, Yamane S, Minami A: Rotator cuff regeneration using chitin fabric as an acellular matrix. J Shoulder Elbow Surg. 2006, 15: 112-118. 10.1016/j.jse.2005.05.012.CrossRefPubMed Funakoshi T, Majima T, Suenaga N, Iwasaki N, Yamane S, Minami A: Rotator cuff regeneration using chitin fabric as an acellular matrix. J Shoulder Elbow Surg. 2006, 15: 112-118. 10.1016/j.jse.2005.05.012.CrossRefPubMed
8.
Zurück zum Zitat Yokoya S, Mochizuki Y, Nagata Y, Deie M, Ochi M: Tendon-bone insertion repair and regeneration using polyglycolic acid sheet in the rabbit rotator cuff injury model. Am J Sports Med. 2008, 36: 1298-1309. 10.1177/0363546508314416.CrossRefPubMed Yokoya S, Mochizuki Y, Nagata Y, Deie M, Ochi M: Tendon-bone insertion repair and regeneration using polyglycolic acid sheet in the rabbit rotator cuff injury model. Am J Sports Med. 2008, 36: 1298-1309. 10.1177/0363546508314416.CrossRefPubMed
9.
Zurück zum Zitat Iannotti JP, Codsi MJ, Kwon YW, Derwin K, Ciccone J, Brems JJ: Porcine small intestine submucosa augmentation of surgical repair of chronic two-tendon rotator cuff tears. A randomized, controlled trial. J Bone Joint Surg Am. 2006, 88: 1238-1244. 10.2106/JBJS.E.00524.CrossRefPubMed Iannotti JP, Codsi MJ, Kwon YW, Derwin K, Ciccone J, Brems JJ: Porcine small intestine submucosa augmentation of surgical repair of chronic two-tendon rotator cuff tears. A randomized, controlled trial. J Bone Joint Surg Am. 2006, 88: 1238-1244. 10.2106/JBJS.E.00524.CrossRefPubMed
10.
Zurück zum Zitat Ozaki J, Fujimoto S, Masuhara K, Tamai S, Yoshimoto S: Reconstruction of chronic massive rotator cuff tears with synthetic materials. Clin Orthop Relat Res. 1986, 173-183. Ozaki J, Fujimoto S, Masuhara K, Tamai S, Yoshimoto S: Reconstruction of chronic massive rotator cuff tears with synthetic materials. Clin Orthop Relat Res. 1986, 173-183.
11.
Zurück zum Zitat Kimura A, Aoki M, Fukushima S, Ishii S, Yamakoshi K: Reconstruction of a defect of the rotator cuff with polytetrafluoroethylene felt graft. Recovery of tensile strength and histocompatibility in an animal model. J Bone Joint Surg Br. 2003, 85: 282-287. 10.1302/0301-620X.85B2.12823.CrossRefPubMed Kimura A, Aoki M, Fukushima S, Ishii S, Yamakoshi K: Reconstruction of a defect of the rotator cuff with polytetrafluoroethylene felt graft. Recovery of tensile strength and histocompatibility in an animal model. J Bone Joint Surg Br. 2003, 85: 282-287. 10.1302/0301-620X.85B2.12823.CrossRefPubMed
12.
Zurück zum Zitat Butler DL, Juncosa-Melvin N, Boivin GP, Galloway MT, Shearn JT, Gooch C, Awad H: Functional tissue engineering for tendon repair: A multidisciplinary strategy using mesenchymal stem cells, bioscaffolds, and mechanical stimulation. J Orthop Res. 2008, 26: 1-9. 10.1002/jor.20456.CrossRefPubMed Butler DL, Juncosa-Melvin N, Boivin GP, Galloway MT, Shearn JT, Gooch C, Awad H: Functional tissue engineering for tendon repair: A multidisciplinary strategy using mesenchymal stem cells, bioscaffolds, and mechanical stimulation. J Orthop Res. 2008, 26: 1-9. 10.1002/jor.20456.CrossRefPubMed
13.
Zurück zum Zitat Inui A, Kokubu T, Makino T, Nagura I, Toyokawa N, Sakata R, Kotera M, Nishino T, Fujioka H, Kurosaka M: Potency of double-layered Poly L-lactic Acid scaffold in tissue engineering of tendon tissue. Int Orthop. 2010, 34: 1327-1332. 10.1007/s00264-009-0917-8.CrossRefPubMed Inui A, Kokubu T, Makino T, Nagura I, Toyokawa N, Sakata R, Kotera M, Nishino T, Fujioka H, Kurosaka M: Potency of double-layered Poly L-lactic Acid scaffold in tissue engineering of tendon tissue. Int Orthop. 2010, 34: 1327-1332. 10.1007/s00264-009-0917-8.CrossRefPubMed
14.
Zurück zum Zitat Sasaki K, Kuroda R, Ishida K, Kubo S, Matsumoto T, Mifune Y, Kinoshita K, Tei K, Akisue T, Tabata Y, Kurosaka M: Enhancement of tendon-bone osteointegration of anterior cruciate ligament graft using granulocyte colony-stimulating factor. Am J Sports Med. 2008, 36: 1519-1527. 10.1177/0363546508316282.CrossRefPubMed Sasaki K, Kuroda R, Ishida K, Kubo S, Matsumoto T, Mifune Y, Kinoshita K, Tei K, Akisue T, Tabata Y, Kurosaka M: Enhancement of tendon-bone osteointegration of anterior cruciate ligament graft using granulocyte colony-stimulating factor. Am J Sports Med. 2008, 36: 1519-1527. 10.1177/0363546508316282.CrossRefPubMed
15.
Zurück zum Zitat Brand JC, Nyland J, Caborn DN, Johnson DL: Soft-tissue interference fixation: bioabsorbable screw versus metal screw. Arthroscopy. 2005, 21: 911-916. 10.1016/j.arthro.2005.05.009.CrossRefPubMed Brand JC, Nyland J, Caborn DN, Johnson DL: Soft-tissue interference fixation: bioabsorbable screw versus metal screw. Arthroscopy. 2005, 21: 911-916. 10.1016/j.arthro.2005.05.009.CrossRefPubMed
16.
Zurück zum Zitat Koh JL, Szomor Z, Murrell GA, Warren RF: Supplementation of rotator cuff repair with a bioresorbable scaffold. Am J Sports Med. 2002, 30: 410-413.PubMed Koh JL, Szomor Z, Murrell GA, Warren RF: Supplementation of rotator cuff repair with a bioresorbable scaffold. Am J Sports Med. 2002, 30: 410-413.PubMed
17.
Zurück zum Zitat Li WJ, Cooper JA, Mauck RL, Tuan RS: Fabrication and characterization of six electrospun poly(alpha-hydroxy ester)-based fibrous scaffolds for tissue engineering applications. Acta Biomater. 2006, 2: 377-385. 10.1016/j.actbio.2006.02.005.CrossRefPubMed Li WJ, Cooper JA, Mauck RL, Tuan RS: Fabrication and characterization of six electrospun poly(alpha-hydroxy ester)-based fibrous scaffolds for tissue engineering applications. Acta Biomater. 2006, 2: 377-385. 10.1016/j.actbio.2006.02.005.CrossRefPubMed
18.
Zurück zum Zitat MacGillivray JD, Fealy S, Terry MA, Koh JL, Nixon AJ, Warren RF: Biomechanical evaluation of a rotator cuff defect model augmented with a bioresorbable scaffold in goats. J Shoulder Elbow Surg. 2006, 15: 639-644. 10.1016/j.jse.2005.11.009.CrossRefPubMed MacGillivray JD, Fealy S, Terry MA, Koh JL, Nixon AJ, Warren RF: Biomechanical evaluation of a rotator cuff defect model augmented with a bioresorbable scaffold in goats. J Shoulder Elbow Surg. 2006, 15: 639-644. 10.1016/j.jse.2005.11.009.CrossRefPubMed
19.
Zurück zum Zitat Dahlgren LA, Mohammed HO, Nixon AJ: Temporal expression of growth factors and matrix molecules in healing tendon lesions. J Orthop Res. 2005, 23: 84-92. 10.1016/j.orthres.2004.05.007.CrossRefPubMed Dahlgren LA, Mohammed HO, Nixon AJ: Temporal expression of growth factors and matrix molecules in healing tendon lesions. J Orthop Res. 2005, 23: 84-92. 10.1016/j.orthres.2004.05.007.CrossRefPubMed
20.
Zurück zum Zitat Hirose K, Kondo S, Choi HR, Mishima S, Iwata H, Ishiguro N: Spontaneous healing process of a supraspinatus tendon tear in rabbits. Arch Orthop Trauma Surg. 2004, 124: 374-377.CrossRefPubMed Hirose K, Kondo S, Choi HR, Mishima S, Iwata H, Ishiguro N: Spontaneous healing process of a supraspinatus tendon tear in rabbits. Arch Orthop Trauma Surg. 2004, 124: 374-377.CrossRefPubMed
21.
Zurück zum Zitat Amiel D, Nagineni CN, Choi SH, Lee J: Intrinsic properties of ACL and MCL cells and their responses to growth factors. Med Sci Sports Exerc. 1995, 27: 844-851.CrossRefPubMed Amiel D, Nagineni CN, Choi SH, Lee J: Intrinsic properties of ACL and MCL cells and their responses to growth factors. Med Sci Sports Exerc. 1995, 27: 844-851.CrossRefPubMed
22.
Zurück zum Zitat Liu SH, Panossian V, al-Shaikh R, Tomin E, Shepherd E, Finerman GA, Lane JM: Morphology and matrix composition during early tendon to bone healing. Clin Orthop Relat Res. 1997, 253-260. Liu SH, Panossian V, al-Shaikh R, Tomin E, Shepherd E, Finerman GA, Lane JM: Morphology and matrix composition during early tendon to bone healing. Clin Orthop Relat Res. 1997, 253-260.
23.
Zurück zum Zitat Liu SH, Yang RS, al-Shaikh R, Lane JM: Collagen in tendon, ligament, and bone healing. A current review. Clin Orthop Relat Res. 1995, 265-278. Liu SH, Yang RS, al-Shaikh R, Lane JM: Collagen in tendon, ligament, and bone healing. A current review. Clin Orthop Relat Res. 1995, 265-278.
24.
Zurück zum Zitat Bostman O, Pihlajamaki H: Clinical biocompatibility of biodegradable orthopaedic implants for internal fixation: a review. Biomaterials. 2000, 21: 2615-2621. 10.1016/S0142-9612(00)00129-0.CrossRefPubMed Bostman O, Pihlajamaki H: Clinical biocompatibility of biodegradable orthopaedic implants for internal fixation: a review. Biomaterials. 2000, 21: 2615-2621. 10.1016/S0142-9612(00)00129-0.CrossRefPubMed
Metadaten
Titel
Application of layered poly (L-lactic acid) cell free scaffold in a rabbit rotator cuff defect model
verfasst von
Atsuyuki Inui
Takeshi Kokubu
Hiroyuki Fujioka
Issei Nagura
Ryosuke Sakata
Hanako Nishimoto
Masaru Kotera
Takashi Nishino
Masahiro Kurosaka
Publikationsdatum
01.12.2011
Verlag
BioMed Central
Erschienen in
BMC Sports Science, Medicine and Rehabilitation / Ausgabe 1/2011
Elektronische ISSN: 2052-1847
DOI
https://doi.org/10.1186/1758-2555-3-29

Weitere Artikel der Ausgabe 1/2011

BMC Sports Science, Medicine and Rehabilitation 1/2011 Zur Ausgabe

Arthropedia

Grundlagenwissen der Arthroskopie und Gelenkchirurgie. Erweitert durch Fallbeispiele, Videos und Abbildungen. 
» Jetzt entdecken

Notfall-TEP der Hüfte ist auch bei 90-Jährigen machbar

26.04.2024 Hüft-TEP Nachrichten

Ob bei einer Notfalloperation nach Schenkelhalsfraktur eine Hemiarthroplastik oder eine totale Endoprothese (TEP) eingebaut wird, sollte nicht allein vom Alter der Patientinnen und Patienten abhängen. Auch über 90-Jährige können von der TEP profitieren.

Arthroskopie kann Knieprothese nicht hinauszögern

25.04.2024 Gonarthrose Nachrichten

Ein arthroskopischer Eingriff bei Kniearthrose macht im Hinblick darauf, ob und wann ein Gelenkersatz fällig wird, offenbar keinen Unterschied.

Therapiestart mit Blutdrucksenkern erhöht Frakturrisiko

25.04.2024 Hypertonie Nachrichten

Beginnen ältere Männer im Pflegeheim eine Antihypertensiva-Therapie, dann ist die Frakturrate in den folgenden 30 Tagen mehr als verdoppelt. Besonders häufig stürzen Demenzkranke und Männer, die erstmals Blutdrucksenker nehmen. Dafür spricht eine Analyse unter US-Veteranen.

Ärztliche Empathie hilft gegen Rückenschmerzen

23.04.2024 Leitsymptom Rückenschmerzen Nachrichten

Personen mit chronischen Rückenschmerzen, die von einfühlsamen Ärzten und Ärztinnen betreut werden, berichten über weniger Beschwerden und eine bessere Lebensqualität.

Update Orthopädie und Unfallchirurgie

Bestellen Sie unseren Fach-Newsletter und bleiben Sie gut informiert.