01.11.2010 | Original Article

Influence of etching time on bond strength in dentin irradiated with erbium lasers

verfasst von: Leila Soares Ferreira, Christian Apel, Carlos Francci, Alyne Simoes, Carlos P. Eduardo, Norbert Gutknecht

Erschienen in: Lasers in Medical Science | Ausgabe 6/2010

Einloggen, um Zugang zu erhalten

Abstract

The purpose of this in vitro study was to evaluate the effect of etching time on the tensile bond strength (TBS) of a conventional adhesive bonded to dentin previously irradiated with erbium:yttrium–aluminum–garnet (Er:YAG) and erbium, chromium:yttrium–scandium–gallium–garnet (Er,Cr:YSGG) lasers. Buccal and lingual surfaces of 45 third molars were flattened until the dentin was exposed and randomly assigned to three groups (n = 30) according to the dentin treatment: control (not irradiated), irradiated with Er:YAG (1 W; 250 mJ; 4 Hz; 80.6 J/cm²) laser or Er,Cr:YSGG (4 W; 200 mJ; 20 Hz; 71.4 J/cm²) laser, and into three subgroups (n = 10) according to acid etching time (15 s, 30 s or 60 s) for each experimental group. After acid etching, the adhesive was applied, followed by the construction of an inverted cone of composite resin. The samples were immersed in distilled water (37°C for 24 h) and subjected to TBS test [50 kilogram-force (kgf), 0.5 mm/min]. Data were analyzed by analysis of variance (ANOVA) and Tukey statistical tests (P ≤ 0.05). Control group samples presented significant higher TBS values than those of all lased groups. Both irradiated groups exhibited similar TBS values. Samples subjected to the different etching times in each experimental group presented similar TBS. Based on the conditions of this in vitro study we concluded that Er:YAG and Er,Cr:YSGG laser irradiation of the dentin weakens the bond strength of the adhesive. Moreover, increased etching time is not able to modify the bonding strength of the adhesive to irradiated dentin.

Eversole LR, Rizoiu I, Kimmel AI (1997) Pulpal response to cavity preparation by an erbium, chromium:YSGG laser-powered hydrokinetic system. J Am Dent Assoc 128:1099–1106PubMed

Hibst R, Keller U (1989) Experimental studies of the application of the Er:YAG laser on dental hard substances: I. Measurement of the ablation rate. Lasers Surg Med 9:338–344CrossRefPubMed

Keller U, Hibst R (1989) Experimental studies of the application of the Er:YAG laser on dental hard substances: II. Light microscopic and SEM investigations. Lasers Surg Med 9:345–351CrossRefPubMed

Hossain M, Nakamura Y, Tamaki Y, Yamada Y, Murakami Y, Matsumoto K (2003) Atomic analysis and knoop hardness measurement of the cavity floor prepared by Er, Cr:YSGG laser irradiation in vitro. J Oral Rehabil 30:515–521CrossRefPubMed

Schein MT, Bocangel JS, Nogueira GE, Schein PA (2003) SEM evaluation of the interaction pattern between dentin and resin after cavity preparation using ER:YAG laser. J Dent 31:127–135CrossRefPubMed

Harashima T, Kinoshita J, Kimura Y, Brugnera A, Zanin F, Pecora JD, Matsumoto K (2005) Morphological comparative study on ablation of dental hard tissues at cavity preparation by Er:YAG and Er, Cr:YSGG lasers. Photomed Laser Surg 23:52–55CrossRefPubMed

Aranha AC, De Paula Eduardo C, Gutknecht N, Marques MM, Ramalho KM, Apel C (2007) Analysis of the interfacial micromorphology of adhesive systems in cavities prepared with Er, Cr:YSGG, Er:YAG laser and bur. Microsc Res Tech 70:745–751CrossRefPubMed

Esteves-Oliveira M, Zezell DM, Apel C, Turbino ML, Aranha AC, Eduardo Cde P, Gutknecht N (2007) Bond strength of self-etching primer to bur cut, Er, Cr:YSGG, and Er:YAG lased dental surfaces. Photomed Laser Surg 25:373–380CrossRefPubMed

Freitas PM, Navarro RS, Barros JA, de Paula Eduardo C (2007) The use of Er:YAG laser for cavity preparation: an SEM evaluation. Microsc Res Tech 70:803–808CrossRefPubMed

10.

Chou JC, Chen CC, Ding SJ (2009) Effect of Er,Cr:YSGG laser parameters on shear bond strength and microstructure of dentine. Photomed Laser Surg 27:481–486

11.

Corona SA, Souza-Gabriel AE, Chinelatti MA, Pecora JD, Borsatto MC, Palma-Dibb RG (2008) Influence of energy and pulse repetition rate of Er:YAG laser on enamel ablation ability and morphological analysis of the laser-irradiated surface. J Biomed Mater Res A 84:569–575PubMed

12.

Youssef M, Quinelato A, Youssef F, Pelino JEP, Salvadori MC, Mori M (2008) Dentinal surface-cutting efficiency using a high-speed diamond bur, ultrasound and laser. Laser Physics 18:472–477CrossRef

13.

de Souza AE, Corona SA, Dibb RG, Borsatto MC, Pecora JD (2004) Influence of Er:YAG laser on tensile bond strength of a self-etching system and a flowable resin in different dentin depths. J Dent 32:269–275CrossRefPubMed

14.

Giachetti L, Scaminaci Russo D, Scarpelli F, Vitale M (2004) SEM analysis of dentin treated with the Er:YAG laser: a pilot study of the consequences resulting from laser use on adhesion mechanisms. J Clin Laser Med Surg 22:35–41CrossRefPubMed

15.

de Carvalho RC, de Freitas PM, Otsuki M, de Eduardo CP, Tagami J (2008) Micro-shear bond strength of Er:YAG-laser-treated dentin. Lasers Med Sci 23:117–124CrossRefPubMed

16.

Ceballos L, Osorio R, Toledano M, Marshall GW (2001) Microleakage of composite restorations after acid or Er-YAG laser cavity treatments. Dent Mater 17:340–346CrossRefPubMed

17.

Gonçalves M, Corona SA, Borsatto MC, Silva PC, Pecora JD (2002) Tensile bond strength of dentin-resinous system interfaces conditioned with Er:YAG laser irradiation. J Clin Laser Med Surg 20:89–93CrossRefPubMed

18.

Martínez-Insua A, Da Silva Dominguez L, Rivera FG, Santana-Penín UA (2000) Differences in bonding to acid-etched or Er:YAG-laser-treated enamel and dentin surfaces. J Prosthet Dent 84:280–288CrossRefPubMed

19.

De Munck J, Van Meerbeek B, Yudhira R, Lambrechts P, Vanherle G (2002) Micro-tensile bond strength of two adhesives to erbium:YAG-lased vs bur-cut enamel and dentin. Eur J Oral Sci 110:322–329CrossRefPubMed

20.

Dunn WJ, Davis JT, Bush AC (2005) Shear bond strength and SEM evaluation of composite bonded to Er:YAG laser-prepared dentin and enamel. Dent Mater 21:616–624CrossRefPubMed

21.

Cardoso MV, Coutinho E, Ermis RB, Poitevin A, Van Landuyt K, De Munck J, Carvalho RC, Lambrechts P, Van Meerbeek B (2008) Influence of Er, Cr:YSGG laser treatment on the microtensile bond strength of adhesives to dentin. J Adhes Dent 10:25–33PubMed

22.

Botta SB, da Ana PA, Zezell DM, Powers JM, Matos AB (2009) Adhesion after erbium, chromium:yttrium-scandium-gallium-garnet laser application at three different irradiation conditions. Lasers Med Sci 24:67–73CrossRefPubMed

23.

Hashimoto M, Ohno H, Kaga M, Sano H, Tay FR, Oguchi H, Araki Y, Kubota M (2002) Over-etching effects on micro-tensile bond strength and failure patterns for two dentin bonding systems. J Dent 30:99–105CrossRefPubMed

24.

Abu-Hanna A, Gordan VV (2004) Evaluation of etching time on dentin bond strength using single bottle bonding systems. J Adhes Dent 6:105–110PubMed

25.

Kayano T, Ochiai S, Kiyono K, Yamamoto H, Nakajima S, Mochizuki T (1989) Effects of Er:YAG laser irradiation on human extracted teeth. J Stomatol Soc Jpn 56:381–392

26.

Kumazaki M, Fujiwara H, Matsuda T, Zennyu K, Kumazaki M, Toyoda K, Fujii B (1992) Excision of dental caries. J Jpn Soc Laser Dent 3:23–27

27.

Rizoiu I, Kohanghadosh F, Kimmel AI, Eversole LR (1998) Pulpal thermal responses to an erbium, chromium: YSGG pulsed laser hydrokinetic system. Oral Surg Oral Med Oral Pathol Oral Radiol Endod 86:220–223CrossRefPubMed

28.

Fried D, Featherstone JD, Visuri SR, Seka WD, Walsh JT (1996) The caries inhibition potential of Er:YAG and Er:YSGG laser radiation. Proc SPIE 2672:73–78CrossRef

29.

Cardoso MV, Coutinho E, Ermis RB, Poitevin A, Van Landuyt K, De Munck J, Carvalho RC, Van Meerbeek B (2008) Influence of dentin cavity surface finishing on micro-tensile bond strength of adhesives. Dent Mater 24:492–501CrossRefPubMed

30.

Malta DAMP, Costa MM, Pelino JEP, de Andrade MF, Lizarelli RFZ (2008) Bond strength of an adhesive system irradiated with Nd:YAG laser in dentin treated with Er:YAG laser. Laser Phys Lett 5:144–150CrossRef

31.

Benazzato P, Stefani A (2003) The effect of Er:YAG laser treatment on dentin collagen: an SEM investigation. J Oral Laser Appl 3:79–81

32.

Manhaes L, Oliveira DC, Marques MM, Matos AB (2005) Influence of Er:YAG laser surface treatment and primer application methods on microtensile bond strength self-etching systems. Photomed Laser Surg 23:304–312CrossRefPubMed

33.

Armengol V, Jean A, Rohanizadeh R, Hamel H (1999) Scanning electron microscopic analysis of diseased and healthy dental hard tissues after Er:YAG laser irradiation: in vitro study. J Endod 25:543–546CrossRefPubMed

34.

Kameyama A, Kawada E, Takizawa M, Oda Y, Hirai Y (2000) Influence of different acid conditioners on the tensile bond strength of 4-META/MMA-TBB resin to Er:YAG laser-irradiated bovine dentin. J Adhes Dent 2:297–304PubMed

35.

Camerlingo C, Lepore M, Gaeta GM, Riccio R, Riccio C, De Rosa A, De Rosa M (2004) Er:YAG laser treatments on dentine surface: micro-Raman spectroscopy and SEM analysis. J Dent 32:399–405CrossRefPubMed

Titel: Influence of etching time on bond strength in dentin irradiated with erbium lasers
verfasst von: Leila Soares Ferreira
Christian Apel
Carlos Francci
Alyne Simoes
Carlos P. Eduardo
Norbert Gutknecht
Publikationsdatum: 01.11.2010
Verlag: Springer-Verlag
Erschienen in: Lasers in Medical Science / Ausgabe 6/2010
Print ISSN: 0268-8921
Elektronische ISSN: 1435-604X
DOI: https://doi.org/10.1007/s10103-009-0715-y

Springer Medizin

Abstract

Bitte loggen Sie sich ein, um Zugang zu diesem Inhalt zu erhalten

Weitere Artikel der Ausgabe 6/2010

Effect of acid etching duration on tensile bond strength of composite resin bonded to erbium:yttrium–aluminium–garnet laser-prepared dentine. Preliminary study

The influence of erbium:yttrium–aluminum–garnet laser ablation with variable pulse width on morphology and microleakage of composite restorations

Laser phototherapy in the treatment of periodontal disease. A review

The effect of erbium, chromium:yttrium–scandium–gallium–garnet laser etching on marginal integrity of a resin-based fissure sealant in primary teeth

Comparison of short-pulsed and long-pulsed 532 nm lasers in the removal of freckles

Use of the erbium, chromium:yttrium–scandium–gallium–garnet laser on human enamel tissues. Influence of the air–water spray on the laser–tissue interaction: scanning electron microscope evaluations