Effect of Nd: YAG laser irradiation on surface properties and bond strength of zirconia ceramics

verfasst von: Li Liu, Suogang Liu, Xiaomeng Song, Qingping Zhu, Wei Zhang

Erschienen in: Lasers in Medical Science | Ausgabe 2/2015

Einloggen, um Zugang zu erhalten

Abstract

This study investigated the effect of neodymium-doped yttrium aluminum garnet (Nd: YAG) laser irradiation on surface properties and bond strength of zirconia ceramics. Specimens of zirconia ceramic pieces were divided into 11 groups according to surface treatments as follows: one control group (no treatment), one air abrasion group, and nine laser groups (Nd: YAG irradiation). The laser groups were divided by applying with different output power (1, 2, or 3 W) and irradiation time (30, 60, or 90 s). Following surface treatments, the morphological characteristics of ceramic pieces was observed, and the surface roughness was measured. All specimens were bonded to resin cement. After, stored in water for 24 h and additionally aged by thermocycling, the shear bond strength was measured. Dunnett's t test and one-way ANOVA were performed as the statistical analyses for the surface roughness and the shear bond strength, respectively, with α = .05. Rougher surface of the ceramics could be obtained by laser irradiation with higher output power (2 and 3 W). However, cracks and defects were also found on material surface. The shear bond strength of laser groups was not obviously increased, and it was significantly lower than that of air abrasion group. No significant differences of the shear bond strength were found among laser groups treated with different output power or irradiation time. Nd: YAG laser irradiation cannot improve the surface properties of zirconia ceramics and cannot increase the bond strength of the ceramics. Enhancing irradiation power and extending irradiation time cannot induce higher bond strength of the ceramics and may cause material defect.

Cavalcanti AN, Foxton RM, Watson TF, Oliveira MT, Giannini M, Marchi GM (2009) Bond strength of resin cements to a zirconia ceramic with different surface treatments. Oper Dent 34:280–287PubMedCrossRef

Zhang W, Masumi SI, Song XM (2010) Bonding property of two resin-reinforced glass-ionomer cements to zirconia ceramic. Quintessence Int 41:e132–140PubMed

Casucci A, Monticelli F, Goracci C, Mazzitelli C, Cantoro A, Papacchini F, Ferrari M (2011) Effect of surface pretreatments on the zirconia ceramic-resin cement microtensile bond strength. Dent Mater 27:1024–1030PubMedCrossRef

Cavalcanti AN, Pilecki P, Foxton RM, Watson TF, Oliveira MT, Gianinni M, Marchi GM (2009) Evaluation of the surface roughness and morphologic features of Y-TZP ceramics after different surface treatments. Photomed Laser Surg 27:473–479PubMedCrossRef

Alghazzawi TF, Lemons J, Liu PR, Essig ME, Janowski GM (2012) The failure load of CAD/CAM generated zirconia and glass-ceramic laminate veneers with different preparation designs. J Prosthet Dent 108:386–393PubMedCrossRef

Martinez-Insua A, Da Silva DL, Rivera FG, Santana-Penin UA (2000) Differences in bonding to acid-etched or Er: YAG laser treated enamel and dentin surfaces. J Prosthet Dent 84:280–288PubMedCrossRef

Queiroz JR, Souza RO, Nogueira Junior L Jr, Ozcan M, Bottino MA (2012) Influence of acid-etching and ceramic primers on the repair of a glass ceramic. Gen Dent 60(2):e79–85PubMed

Ozcan M, Valandro LF, Amaral R, Leite F, Bottino MA (2009) Bond strength durability of a resin composite on a reinforced ceramic using various repair systems. Dent Mater 25:1477–1483PubMedCrossRef

Borges GA, Sophr AM, de Goes MF, Sobrinho LC, Chan DC (2003) Effect of etching and airborne particle abrasion on the microstructure of different dental ceramics. J Prosthet Dent 89:479–488PubMedCrossRef

10.

Piascik JR, Swift EJ, Thompson JY, Grego S, Stoner BR (2009) Surface modification for enhanced silanation of zirconia ceramics. Dent Mater 25:1116–1121PubMedCentralPubMedCrossRef

11.

Kara HB, Ozturk AN, Aykent F, Koc O, Ozturk B (2011) The effect of different surface treatments on roughness and bond strength in low fusing ceramics. Lasers Med Sci 26:599–604PubMedCrossRef

12.

Kern M, Barloi A, Yang B (2009) Surface conditioning influences zirconia ceramic bonding. J Dent Res 88:817–822PubMedCrossRef

13.

Zhang Y, Lawn BR, Rekow ED, Thompson VP (2004) Effect of sandblasting on the long-term performance of dental ceramics. J Biomed Mater Res B Appl Biomater 71:381–386PubMedCrossRef

14.

Birang R, Poursamimi J, Gutknecht N, Lampert F, Mir M (2007) Comparative evaluation of the effects of Nd: YAG and Er: YAG laser in dentin hypersensitivity treatment. Lasers Med Sci 22:21–24PubMedCrossRef

15.

Harris DM, White JM, Goodis H, Arcoria CJ, Simon J, Carpenter WM, Fried D, Burkart J, Yessik M, Myers T (2002) Selective ablation of surface enamel caries with a pulsed Nd: YAG dental laser. Lasers Surg Med 30:342–350PubMedCrossRef

16.

Marcondes M, Paranhos MP, Spohr AM, Mota EG, da Silva IN, Souto AA, Burnett LH Jr (2009) The influence of the Nd: YAG laser bleaching on physical and mechanical properties of the dental enamel. J Biomed Mater Res B Appl Biomater 90:388–395PubMed

17.

Spohr AM, Borges GA, Júnior LH, Mota EG, Oshima HM (2008) Surface modification of In-Ceram zirconia ceramic by Nd: YAG laser, Rocatec system, or aluminum oxide sandblasting and its bond strength to a resin cement. Photomed Laser Surg 26:203–208PubMedCrossRef

18.

da Silveira BL, Paglia A, Burnett LH, Shinkai RS, de Eduardo CP, Spohr AM (2005) Micro-tensile bond strength between a resin cement and an aluminous ceramic treated with Nd: YAG laser, Rocatec system, or aluminum oxide sandblasting. Photomed Laser Surg 23:543–548PubMedCrossRef

19.

Li R, Ren Y, Han G (2000) Effects of Nd: YAG laser irradiation on shear bond strength of composite resin bonded to porcelain. Hua Kou Qiang yi Xue Za Zhi 18:377–379

20.

Foxton RM, Cavalcanti AN, Nakajima M, Pilecki P, Sherriff M, Melo L, Watson TF (2011) Durability of resin cement bond to aluminum oxide and zirconia ceramics after air abrasion and laser treatment. J Prosthodont 20:84–92PubMedCrossRef

21.

International Organization for Standardization (1998) Polymer-based, Crown and Bridge Materials, ISO10477, Amendment 1

22.

Usumez A, Hamdemirci N, Koroglu BY, Simsek I, Parlar O, Sari T (2013) Bond strength of resin cement to zirconia ceramic with different surface treatments. Lasers Med Sci 28:259–266PubMedCrossRef

23.

Ersu B, Yuzugullu B, Yazici AR, Canay S (2009) Surface roughness and bond strengths of glass-infiltrated alumina-ceramics prepared using various surface treatments. J Dent 37:848–856PubMedCrossRef

24.

Paranhos MP, Burnett LH Jr, Magne P (2011) Effect of Nd: YAG laser and CO2 laser treatment on the resin bond strength to zirconia ceramic. Quintessence Int 42:79–89PubMed

25.

Akyıl MS, Uzun IH, Bayındır F (2010) Bond strength of resin cement to yttrium-stabilized tetragonal zirconia ceramic treated with air abrasion, silica coating, and laser irradiation. Photomed Laser Surg 28:801–808PubMedCrossRef

26.

Noda M, Okuda Y, Tsuruki J, Minesaki Y, Takenouchi Y, Ban S (2010) Surface damages of zirconia by Nd: YAG dental laser irradiation. Dent Mater J 29:536–541PubMedCrossRef

27.

Gökçe B, Ozpinar B, Dündar M, Cömlekoglu E, Sen BH, Güngör MA (2007) Bond strengths of all-ceramics: acid versus laser etching. Oper Dent 32:173–178PubMedCrossRef

28.

Akın H, Ozkurt Z, Kırmalı O, Kazazoglu E, Ozdemir AK (2011) Shear bond strength of resin cement to zirconia ceramic after aluminum oxide sandblasting and various laser treatments. Photomed Laser Surg 29:797–802PubMedCrossRef

29.

Kohorst P, Borchers L, Strempel J, Stiesch M, Hassel T, Bach FW, Hübsch C (2012) Low temperature degradation of different zirconia ceramics for dental applications. Acta Biomater 8:1213–1220PubMedCrossRef

30.

Valandro LF, Della Bona A, Bottino MA, Neisser MP (2005) The effect of ceramic surface treatment on bonding to densely sintered alumina ceramic. J Prosthet Dent 93:253–259PubMedCrossRef

31.

Rocha Gomes Torres C, Caneppele TM, Moral D, de Lazari R, Ribeiro CF, Borges AB (2012) Effect of dental surface treatment with Nd: YAG and Er: YAG lasers on bond strength of resin composite to recently bleached enamel. Lasers Med Sci 27:755–760PubMedCrossRef

32.

Marimoto A, Cunha L, Yui K, Huhtala M, Barcellos D, Prakki A, Gonçalves S (2012) Influence of Nd: YAG Laser on the Bond Strength of Self-etching and Conventional Adhesive Systems to Dental Hard Tissues. Oper Dent [Epub ahead of print]

33.

van As G (2004) Erbium lasers in dentistry. Dent Clin North Am 48:1017–1059PubMedCrossRef

34.

Coluzzi DJ (2004) Fundamentals of dental lasers: science and instruments. Dent Clin North Am 48:751–770PubMedCrossRef

35.

D'Amario M, Campidoglio M, Morresi AL, Luciani L, Marchetti E, Baldi M (2010) Effect of thermocycling on the bond strength between dual-cured resin cements and zirconium-oxide ceramics. J Oral Sci 52:425–430PubMedCrossRef

36.

Toledano M, Osorio R, Osorio E, Aguilera FS, Yamauti M, Pashley DH, Tay F (2007) Durability of resin–dentin bonds: effects of direct/indirect exposure and storage media. Dent Mater 23:885–892PubMedCrossRef

37.

Phark JH, Duarte S Jr, Blatz M, Sadan A (2009) An in vitro evaluation of the long-term resin bond to a new densely sintered high-purity zirconium oxide ceramic surface. J Prosthet Dent 101:29–38PubMedCrossRef

Titel: Effect of Nd: YAG laser irradiation on surface properties and bond strength of zirconia ceramics
verfasst von: Li Liu
Suogang Liu
Xiaomeng Song
Qingping Zhu
Wei Zhang
Publikationsdatum: 01.02.2015
Verlag: Springer London
Erschienen in: Lasers in Medical Science / Ausgabe 2/2015
Print ISSN: 0268-8921
Elektronische ISSN: 1435-604X
DOI: https://doi.org/10.1007/s10103-013-1381-7

Springer Medizin

Abstract

Bitte loggen Sie sich ein, um Zugang zu diesem Inhalt zu erhalten

Weitere Artikel der Ausgabe 2/2015

Ultrashort pulsed laser conditioning of human enamel: in vitro study of the influence of geometrical processing parameters on shear bond strength of orthodontic brackets

Shear bond strength and ultrastructural interface analysis of different adhesive systems to Er:YAG laser-prepared dentin

Effects of Er: YAG laser irradiation on wettability, surface roughness, and biocompatibility of SLA titanium surfaces: an in vitro study

Reply to comments on: “Efficacy of low-level laser therapy in the management of orthodontic pain: a systematic review and meta-analysis”

Effect of Nd: YAG laser on the apical seal after root-end resection and MTA retrofill: a bacterial leakage study

Comparative clinical study of light analgesic effect on temporomandibular disorder (TMD) using red and infrared led therapy