Tensile bond strength of silicone-based soft denture liner to two chemically different denture base resins after various surface treatments

verfasst von: Hakan Akin, Faik Tugut, Umit Guney, Omer Kirmali, Turker Akar

Erschienen in: Lasers in Medical Science | Ausgabe 1/2013

Einloggen, um Zugang zu erhalten

Abstract

This study evaluated the effect of various surface treatments on the tensile bond strength of a silicone-based soft denture liner to two chemically different denture base resins, heat-cured polymethyl methacrylate (PMMA), and light-activated urethane dimethacrylate or Eclipse denture base resin. PMMA test specimens were fabricated and relined with a silicone-based soft denture liner (group AC). Eclipse test specimens were prepared according to the manufacturer’s recommendation. Before they were relined with a silicone-based soft denture liner, each received one of three surface treatments: untreated (control, group EC), Eclipse bonding agent applied (group EB), and laser-irradiated (group EL). Tensile bond strength tests (crosshead speed = 5 mm/min) were performed for all specimens, and the results were analyzed using the analysis of variance followed by Tukey’s test (p = 0.05). Eclipse denture base and PMMA resins presented similar bond strengths to the silicone-based soft denture liner. The highest mean force was observed in group EL specimens, and the tensile bond strengths in group EL were significantly different (p < 0.05) from those in the other groups.

Machado C, Sanchez E, Azer SS, Uribe JM (2007) Comparative study of the transverse strength of three denture base materials. J Dent 35(12):930–933PubMedCrossRef

Katsumata Y, Hojo S, Hamano N, Watanabe T, Yamaguchi H, Okada S, Teranaka T, Ino S (2009) Bonding strength of autopolymerizing resin to nylon denture base polymer. Dent Mater J 28(4):409–418PubMedCrossRef

Yunus N, Rashid AA, Azmi LL, Abu-Hassan MI (2005) Some flexural properties of a nylon denture base polymer. J Oral Rehabil 32:65–71PubMedCrossRef

Ahmad F, Dent M, Yunus N (2009) Shear bond strength of two chemically different denture base polymers to reline materials. J Prosthodont 18(7):596–602PubMedCrossRef

Fletcher-Stark ML, Chung K-H, Rubenstein JE, Raigrodski AJ, Mancl LA (2011) Shear bond strength of denture teeth to heat- and light-polymerized denture base resin. J Prosthodont 20:52–59PubMedCrossRef

Machado AL, Puckett AD, Breeding LC, Wady AF, Vergani CE (2011) Effect of thermocycling on the flexural and impact strength of urethane-based and high-impact denture base resins. Gerodontology. doi:10.1111/j.1741-2358.2011.00474.x

Ali IL, Yunus N, Abu-Hassan MI (2008) Hardness, flexural strength, and flexural modulus comparisons of three differently cured denture base systems. J Prosthodont 17(7):545–549PubMedCrossRef

Diaz-Arnold AM, Vargas MA, Shaull KL, Laffoon JE, Qian F (2008) Flexural and fatigue strengths of denture base resin. J Prosthet Dent 100(1):47–51PubMedCrossRef

Pfeiffer P, An N, Schmage P (2008) Repair strength of hypoallergenic denture base materials. J Prosthet Dent 100(4):292–301PubMedCrossRef

10.

Mese A, Guzel KG (2008) Effect of storage duration on the hardness and tensile bond strength of silicone- and acrylic resin based resilient denture liners to a processed denture base acrylic resin. J Prosthet Dent 99(2):153–159PubMedCrossRef

11.

McCabe JF, Carrick TE, Kamohara H (2002) Adhesive bond strength and compliance for denture soft lining materials. Biomaterials 23:1347–1352PubMedCrossRef

12.

Hatamleh MM, Maryan CJ, Silikas N, Watts DC (2010) Effect of net fiber reinforcement surface treatment on soft denture liner retention and longevity. J Prosthodont 19:258–262PubMedCrossRef

13.

Machado AL, Breeding LC, Puckett AD (2005) Effect of microwave disinfection on the hardness and adhesion of two resilient liners. J Prosthet Dent 94:183–189PubMedCrossRef

14.

Akin H, Tugut F, Mutaf B, Akin G, Ozdemir AK (2011) Effect of different surface treatments on tensile bond strength of silicone based soft denture liner. Lasers Med Sci 26:783–788

15.

Tugut F, Akin H, Mutaf B, Akin G, Ozdemir AK (2012) Strength of the bond between a silicone lining material and denture resin after Er:YAG laser treatments with different pulse durations and levels of energy. Lasers Med Sci Lasers Med Sci 27:281–285

16.

Akin H, Tugut F, Mutaf B, Guney U, Ozdemir AK (2011) Effect of sandblasting with different size of aluminum oxide particles on tensile bond strength of resilient liner to denture base. Cumhuriyet Dent J 14(1):5–11

17.

Usumez A, Inan O, Aykent F (2004) Bond strength of a silicone lining material to alumina-abraded and lased denture resin. J Biomed Mater Res Part B: Appl Biomater 71:196–200CrossRef

18.

Jacobsen NL, Mitchell DL, Johnson DL, Holt RA (1997) Lased and sandblasted denture base surface preparations affecting resilient liner bonding. J Prosthet Dent 78:153–158PubMedCrossRef

19.

Kulak-Ozkan Y, Sertgoz A, Gedik H (2003) Effect of thermocycling on tensile bond strength of six silicone-based, resilient denture liners. J Prosthet Dent 89:303–310PubMedCrossRef

20.

Botega DM, Sanchez JL, Mesquita MF, Henriques GE, Consani RL (2008) Effects of thermocycling on the tensile bond strength of three permanent soft denture liners. J Prosthodont 17:550–554PubMedCrossRef

21.

Aydin AK, Terzioğlu H, Akinay AE, Ulubayram K, Hasirci N (1999) Bond strength and failure analysis of lining materials to denture resin. Dent Mater 15:211–218PubMedCrossRef

22.

Kawano F, Dootz ER, Koran A 3rd, Craig RG (1992) Comparison of bond strength of six soft denture liners to denture base resin. J Prosthet Dent 68:368–371PubMedCrossRef

23.

Mutluay MM, Ruyter IE (2007) Evaluation of bond strength of soft relining materials to denture base polymers. Dent Mater 23:1373–1381PubMedCrossRef

24.

Storer R (1962) Resilient denture base materials. Part 1, introduction and laboratory evaluation. Br Dent J 113:195–203

25.

Amin WM, Fletcher AM, Ritchie GM (1981) The nature of the interface between polymethyl methacrylate denture base materials and soft lining materials. J Dent 9:336–346PubMedCrossRef

26.

Lawrence J, Li L (2001) Modification of the wettability characteristics of polymethyl methacrylate (PMMA) by means of CO2, Nd:YAG, excimer and high power diode laser radiation. Mater Sci Eng, A 303:142–149CrossRef

27.

Mutluay MM, Ruyter IE (2005) Evaluation of adhesion of chairside hard relining materials to denture base polymers. J Prosthet Dent 94:445–452PubMedCrossRef

28.

Arena CA, Evans DB, Hilton TJ (1993) A comparison of bond strengths among chairside hard reline materials. J Prosthet Dent 70:126–131PubMedCrossRef

29.

Leles CR, Machado AL, Vergani CE, Giampaolo ET, Pavarina AC (2001) Bonding strength between a hard chairside reline resin and a denture base material as influenced by surface treatment. J Oral Rehabil 28:1153–1157PubMedCrossRef

30.

Al-Athel MS, Jagger RG (1996) Effect of test method on the bond strength of a silicone resilient denture lining material. J Prosthet Dent 76:535–540PubMedCrossRef

31.

ASTM D 429–81 (1998) Standard Test Methods for Rubber Property—adhesion to rigid substrates. Annual book of ASTM standards. ASTM, West Consohocken

Titel: Tensile bond strength of silicone-based soft denture liner to two chemically different denture base resins after various surface treatments
verfasst von: Hakan Akin
Faik Tugut
Umit Guney
Omer Kirmali
Turker Akar
Publikationsdatum: 01.01.2013
Verlag: Springer-Verlag
Erschienen in: Lasers in Medical Science / Ausgabe 1/2013
Print ISSN: 0268-8921
Elektronische ISSN: 1435-604X
DOI: https://doi.org/10.1007/s10103-012-1082-7

Springer Medizin

Abstract

Bitte loggen Sie sich ein, um Zugang zu diesem Inhalt zu erhalten

Weitere Artikel der Ausgabe 1/2013

Effect of surface pretreatment with two desensitizer techniques on the microleakage of resin composite restorations

The effect of He-Ne and Ga-Al-As laser light on the healing of hard palate mucosa of mice

Analgesic effect of a low-level laser therapy (830 nm) in early orthodontic treatment

Influence of cross-infection control methods on performance of pen-type laser fluorescence in detecting occlusal caries lesions in primary teeth

The effect of Nd:YAG and Er,Cr:YSGG lasers on the microhardness of human dentin

Proinflammatory cytokine levels in saliva in patients with burning mouth syndrome before and after treatment with low-level laser therapy