Tibial geometry is associated with failure load ex vivo: a MRI, pQCT and DXA study
verfasst von:
D. Liu, S. L. Manske, S. A. Kontulainen, C. Tang, P. Guy, T. R. Oxland, H. A. McKay
Erschienen in:
Osteoporosis International
|
Ausgabe 7/2007
Einloggen, um Zugang zu erhalten
Abstract
Summary
We studied the relations between bone geometry and density and the mechanical properties of human cadaveric tibiae. Bone geometry, assessed by MRI and pQCT, and bone density, assessed by DXA, were significantly associated with bone’s mechanical properties. However, cortical density assessed by pQCT was not associated with mechanical properties.
Introduction
The primary objective of this study was to determine the contribution of cross-sectional geometry (by MRI and pQCT) and density (by pQCT and DXA) to mechanical properties of the human cadaveric tibia.
Methods
We assessed 20 human cadaveric tibiae. Bone cross-sectional geometry variables (total area, cortical area, and section modulus) were measured with MRI and pQCT. Cortical density and areal BMD were measured with pQCT and DXA, respectively. The specimens were tested to failure in a four-point bending apparatus. Coefficients of determination between imaging variables of interest and mechanical properties were determined.
Results
Cross-sectional geometry measurements from MRI and pQCT were strongly correlated with bone mechanical properties (r2 range from 0.55 to 0.85). Bone cross-sectional geometry measured by MRI explained a proportion of variance in mechanical properties similar to that explained by pQCT bone cross-sectional geometry measurements and DXA measurements.
Conclusions
We found that there was a close association between geometry and mechanical properties regardless of the imaging modality (MRI or pQCT) used.